Information × Registration Number 2112U001604, Article popup.category Thesis Title popup.author popup.publication 01-01-2012 popup.source_user Сумський державний університет popup.source http://essuir.sumdu.edu.ua/handle/123456789/34885 popup.publisher Sumy State University Description Nanostructured Ti6Al4V alloy was successfully formed through mechanical alloying of a stoichiometric mixture of Ti, Al and V powders. Phase evolutions of the milled powders were investigated by XRD. The Ti(Al,V) solid solution formed after 10 h milling. Prolongation of the milling process up to 20 h lead to a structure consisting of the B-Ti phase in the a-Ti(Al) matrix. The nanostructured Ti6Al4V alloy had a grain size and hardness of 20 nm and 600 Hv respectively. Thermal stability of the alloyed powder was good as it's hardness increased to 950 Hv after 5 hr heat treatment at 1100 degrees Celsius. When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/34885 popup.nrat_date 2025-05-12 Close