Інформація × Реєстраційний номер 2112U001404, Матеріали видань та локальних репозитаріїв Категорія Thesis Назва роботи Carrier Density Dependence of sp-d Exchange in Nanostructured ZnO:Mn Thin Film Автор Дата публікації 01-01-2012 Постачальник інформації Сумський державний університет Першоджерело http://essuir.sumdu.edu.ua/handle/123456789/34907 Видання Sumy State University Опис In this work, the nanostructured ZnO:Mn thin films with different Mn concentration (5, 10 and 15 mol%) have been grown on glass substrates at 500°C by the spray pyrolysis technique. The average grain size was estimated about 25 nm using SEM micrographs. The Faraday rotations were determined in applied magnetic fields up to 1.05 T. The highest values of Faraday rotation were observed in the sample with 5 mol% Mn concentration. The carrier density has been calculated from the Faraday rotations and it is observed that the sp-d exchange in magnetic semiconductor is strongly affected by carrier parameters. When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/34907 Додано в НРАТ 2025-05-12 Закрити
Матеріали
Thesis
Carrier Density Dependence of sp-d Exchange in Nanostructured ZnO:Mn Thin Film
Carrier Density Dependence of sp-d Exchange in Nanostructured ZnO:Mn Thin Film : публікація 2012-01-01; Сумський державний університет, 2112U001404
Знайдено документів: 1

Оновлено: 2026-04-09


Роздрукувати цю сторінку